Ultra Thin Ultra Clear Aluminosilicate Glass For Anti-reflective Display Cover Glass
Alumino-Silicate Glass (CHIYAN-M2) is an eco-friendly high aluminosilicate ultra-thin glass, which increases the Al₂O₃ content in the composition to improve the ion exchange efficiency, so that it has excellent mechanical properties after chemical strengthening.
Features:
High Impact Resistance
High Scratch Resistance
High Transmittance
High chemical resistance
High Flexibility
High Bending Strength Resistance
Ultra Clear White
CHIYAN-M2’s 0.25~2.5mm thickness high alumino-silicate glass has already been used in the market to meet a wide range of customers needs.
Application: Widely used in High-end Consumer Electronics Device Cover such as cellphone, tablet, laptop, computer display, Vehicle Display, Industrial Touch Panels, Smart Home Screen Display etc fields;
Regular Thickness: 0.25mm~2mm
Standard Size:1300*1100mm (5th Generation)
Note: The size can be customized according to customer's needs.
Product Composition
Alumino-Silicate Glass achieves better stress and strain depth than ordinary soda-lime glass by increasing the Al₂O₃ content in the glass and increasing the ion exchange capacity.
Physical Property Parameter
|
S/N |
Items |
Unit |
CY-M2 |
|
1 |
Density |
g/cm3 |
2.47 |
|
2 |
Refractive Index(590nm) |
/ |
1.51 |
|
3 |
Young's Modulus |
Gpa |
75.6 |
|
4 |
Shear Modulus |
Gpa |
30.7 |
|
5 |
Volume Resistivity |
lg(Ω .cm) |
9.1 |
|
6 |
Dielectric Constant |
F/m |
8.2 |
|
7 |
Softening Point |
℃ |
830 |
|
8 |
Strain Point |
℃ |
558 |
|
9 |
Annealing Point |
℃ |
606 |
|
10 |
Transmittance(0.7mmt,550nm) |
% |
≥92 |
|
11 |
Thermal Expansivity |
* 10-7/℃ |
98 |
|
12 |
Photoelastic Coefficient |
nm/cm/MPa |
27.2 |
|
13 |
Poisson's Coefficient |
/ |
0.23 |
|
14 |
Vickers-hardness |
HV |
700 |
Chemical Tempering Process Parameter
|
CS |
>900Mpa |
|
DOL |
>50um |
|
4PB |
>800Mpa |
Note: Tempering solution Na+<0.5%. The above test results are affected by processing conditions, the data is for reference only, not as a basis for production.
Packaging Diagram
Storage Conditions: Temperature ≤30℃, humidity ≤65% (no condensation), shelf life is 6 months from the date of delivery.
High Alumino-Silicate Glass(CHIYAN-H1) is adopted Float Glass Process.
Float glass is made by heating raw materials—silica sand, limestone, soda ash, and magnesium in a furnace. When melted, it’s then spread out over a sizable bed of molten tin. As it moves along rollers in the annealing oven during a controlled cooling process, this mixture slowly solidifies over the molten tin. From this point, a single, continuous smooth ribbon of glass emerges as below picture showed: